The present research work was carried out in order to assess the quality of four Syrian cotton varieties namely: Deir-22, Aleppo 33/1, Aleppo 90, and Aleppo 118. HVI was used to investigate the characteristics of the fibers at Cotton Arbitration and Testing General Organization, Alexandria, Egypt (2010-2011). Physical and Mechanical properties of the fibers were measured for the Syrian cotton studied varieties and some other parameters were also studied as it was possible to do on the HVI. The tested fibers were spun on ring spinning system with 40's count at Cotton Research Institute, Cairo Egypt. The produced yarns were tested for lea strength, single yarn strength and yarn elongation. The result revealed that the length of the Syrian Cotton varieties studied were ranged between 30 and 32.5 mm. in which Deir-22 fibers were the lowest and Aleppo 90 fibers were the highest in length. Values of Aleppo 118 and Aleppo 33/1 were 31.86 and 32.23 mm., respectively. Values of fiber strength (g/tex) were recorded for Aleppo 90, Deir -22, Aleppo 33/1 and Aleppo 118 as 31.3, 31.5, 36.1 and 36.5, respectively. Fiber elongation characteristic was recorded for the four Syrian cotton varieties and it was found to be the highest for Deir-22 with value of 5.8 % followed by 5.7% for Aleppo 33/1 and 5,2% for both of Aleppo 90 and Aleppo 118.

The best single yarn strength and yarn elongation were recorded as 17.74 g/tex and 5.77 % for Deir -22 , while no significant differences were observed between the rest of the studied varieties. However, the lowest value of yarn elongation 4.99 was recorded for Aleppo 118. Differences between values of lea strength for the four varieties were found non-significant.

Key Words: Fiber Quality Characteristics, Fiber physical Properties, Cotton Yarns.

 تم إجراء البحث الحالي من أجل تقييم جودة أربعة أصناف من القطن السوري وهي: دير 22 ، حلب 33/1 ، حلب 90 ، حلب 118. تم استخدام HVI للتحقيق في خصائص الألياف في تحكيم القطن و المؤسسة العامة للاختبارات ، الإسكندرية ، مصر (2010-2011). تم قياس الخواص الفيزيائية والميكانيكية للألياف بالنسبة للأصناف المدروسة من القطن السوري ، كما تمت دراسة بعض البارامترات الأخرى حيث كان من الممكن القيام بها على HVI. تم نسج الألياف المختبرة على نظام الغزل الحلقي بعدد الأربعينات في معهد بحوث القطن ، القاهرة ، مصر. تم اختبار الخيوط التي تم إنتاجها للتأكد من صغرها وقوة الغزل الفردية وإطالة الخيوط. كشفت النتيجة أن طول أصناف القطن السوري المدروسة تراوحت بين 30 و 32.5 ملم. حيث كانت ألياف دير 22 هي الأدنى والألياف حلب 90 كانت الأعلى في الطول. كانت قيم حلب 118 وحلب 33/1 31.86 و 32.23 ملم على التوالي. تم تسجيل قيم قوة الألياف (g / tex) في حلب 90 ودير 22 وحلب 33/1 وحلب 118 في 31.3 و 31.5 و 36.1 و 36.5 على التوالي. تم تسجيل خاصية استطالة الألياف للأصناف الأربعة من القطن السوري ووجد أنها الأعلى في دير 22 بقيمة 5.8٪  تلاه 5.7٪ في حلب 33/1 و 5،2٪ لكل من حلب 90 و حلب 118.