The aim of this work is to study the thermal surface treatment by Aluminizing process of stainless steel (305) to modify the mechanical properties of the surface by pack cementation process. The coating process was done with various period of time (2, 4, 6, 8, 10 hours and temperatures (900, 1000, 1100) Co. The results showed that the thickness of coating layer was increased with the increment of time and temperature. The micro hardness values of coating layer was reduced from the outer surface to the core, also the results showed that the highest micro hardness of the coating was obtained at period of (6) hours and temperature of (900, 1000, 1100) C°, also the highest bending stress was obtained at the period of (6) hours and at all temperature.

تناول البحث أجراء معالجة كيميا حرارية سطحية لتحرير الخصائص الميكانيكية لسطح السبيكة الأساس وهو السطح السبائكي لسطح السبيكة الأساس وهو السطح السبائكي (305) باستعمال واحدة من طرق المعالجات الكيميا حرارية  للسطح (التغليف), وهي عملية المعالجة بالألمنيوم (الألمنة) وهي واحدة من طرق الطلاء الانتشاري حيث تمت عملية الطلاء بالألمنيوم بدرجات حرارية (1200_1000_900)م, ولفترات زمنية (10-8-6-4-2) ساعة.

وقد تم قياس سماكة طبقة سماكة طبقة الطلاء تزداد بزيادة درجة الحرارة والزمن , كما تم قياس الصلادة الميكروية ووجد أن مقدار الصلادة الميكروية يزداد عند الأطراف ويقل كلما اتجهنا نحو القلب . وان أفضل مقدار للصلادة حصلنا عليه :

عند زمن (6)ساعة, لدرجات الحرارية (1100 _ 1000 _ 900)م.

وكذلك تم قياس إجهاد الانحناء ووجد إن أفضل قيمة لإجهاد الانحناء حصلنا عليها عند زمن (6)ساعة وللدرجات الحرارية الثلاث .

الكلمات المفتاحية : الألمنة , الانتشار , السماكة , الصلادة الميكروية , إجهاد انحناء .