 Solar cell Multilayers  with CdSe quantum dots was prepared using nanotechnology. The prepared solar cell showed an ideal character for solar cell. The efficiency of the prepared cell was 21.5%. The frequency response of the solar cell was studied as a function of wavelength of light . The cell showed several response peaks that corresponded to wavelengths (450-530-650)nm. The radii of the formed quantum dots were calculated using a semi-empirical relationship. The I-V feature of the cell was studied and found to be close to the ideal feature of the solar cell. The filling factor and yield of this cell were calculated. The yield was relatively small compared to some laboratory cells. The frequency response of this cell was studied and it was noted that the cell response increased with increasing wavelength. The quantum conversion rate was greatest at wavelength 610 nm, where the quantum conversion reached 21%.

 تم تحضير خلايا شمسية متعددة الطبقات ذات النقاط الكوانتية CdSe  باستخدام تقانة النانوية،  أبدت الخلية الشمسية المحضرة ميزة شبه مثالية تمتلك خواص الوصلة الثنائية، كان مردود الخلية المحضرة 21.5%  . دُرست الاستجابة الترددية للخلية الشمسية بتابعية طول الموجة ، أظهرت الخلية عدة قمم استجابة وافقت أطوال موجية (450- 530-650)nm . تم حساب انصاف اقطار النقاط الكوانتية المتشكلة باستخدام علاقة نصف تجريبية ، ُدرست الميزة I-V  للخلية ووجد انها قريبة من الميزة المثالية للخلية الشمسية . تم حساب عامل الملء ومرود هذه الخلية ، كان المردود صغير نسبياً قياساً ببعض الخلايا المخبرية ، درست الاستجابة الترددية لهذه الخلية ولوحظ زيادة استجابة الخلية مع زيادة الطول الموجي . كان معدل التحويل الكوانتي أكبر ما يمكن عند الطول 610 nm  حيث بلغ التحويل الكوانتي 21%.