 A solar cell with multilayer quantum dots (QDs) was prepared, one of the electrodes being transparent (FTO) and the other opaque (AL). The I-V feature of the prepared cell showed stability of the current (I = 0.012mA) at low potentials. The highest value of the cell current was a potential of 8.4 v, and the maximum load power was 0.1μW. The yield of this cell is 7.14%. A study of the response of the cell current to the wavelength falling on it showed that there were two peaks of the response. The first was at the beginning of the visible spectrum at a wavelength of 450nm, corresponding to a current intensity of 0.038mA, and the second peak was in the red color region at a wavelength of 610nm, corresponding to a current intensity of 0.021mA. The quantum conversion rate increased with increasing wavelength within the visible range. The quantum conversion rate was greatest at the length of 610 nm, where the quantum conversion reached 21.58%.

 تم تحضير خلية شمسية ذات نقاط كمية QDs متعددة الطبقات أحد أقطابها شفاف FTO والأخر عاتم AL .أبدت الميزة I-V للخلية المحضرة ثبات التيار(I=0.012mA) عند الكمونات المنخفضة ، أعلى قيمة لتيار الخلية وافقت الكمون 8.4 v  كانت استطاعة الحمل الاعظمي 0.1μW .  ومرود هذه الخلية 7.14% ، بيَنت دراسة الاستجابة تيار الخلية للطول الموجي الساقط عليها وجود قمتين للاستجابة الأولى كانت عند منطقة بداية الطيف المرئي عند الطول الموجي 450nm وافقت شدة تيار 0.038mA والقمة الثانية في منطقة اللون الأحمر عند الطول الموجي 610nm وافقت شدة تيار 0.021mA. ازداد معدل التحويل الكوانتي مع زيادة الطول الموجي ضمن المجال المرئي ، كان معدل التحويل الكوانتي أكبر ما يمكن عند الطول 610 nm  حيث بلغ التحويل الكوانتي 21.58%.